Abstract The aim was to evaluate the effect of 2% grape seed extract (GSE) containing phosphoric acid (PhA) on the bond strength to enamel and dentin. The control group was 37% PhA. The following three PhA formulations with 2% GSE and 20% ethanol were obtained: GSE5 = 5% PhA; GSE10 = 10% PhA; and GSE20 = 20% PhA. The enamel and dentin surfaces of molars were etched with the acid solutions, followed by Scotchbond Multi-Purpose adhesive and composite resin application. The tensile bond strength (TBS) test evaluated the bond to enamel after 24 h, and the microtensile bond strength (μTBS) test evaluated the bond to dentin after 24 h and 12-month water storage. Etched enamel and dentin were observed by scanning electron microscopy (SEM) and atomic force microscopy (AFM), respectively. The TBS data were submitted to one-way ANOVA, while µTBS data were submitted to two-way ANOVA and Tukey’s test (α = 0.05). The TBS (MPa) to enamel did not significantly differ among the control (48.1 ± 15.7), GSE5 (46.1 ± 9.6), GSE10 (49.8 ± 13.6) and GSE20 (44.1 ± 11.9) groups (p = 0.537). The µTBS (MPa) to dentin of the control (28.4 ± 14.4) and GSE20 (24.1 ± 8.1) groups were significantly higher than those of the GSE5 (16.8 ± 7.4) and GSE10 (17.5 ± 6.6) groups at 24 h (p < 0.006). After 12-month storage, only GSE5 (21.0 ± 7.8) and GSE10 (17.6 ± 8.0) did not show significantly decreased μTBS (p > 0.145). SEM micrographs showed a shallower enamel etching pattern for GSE5. AFM images showed the formation of collagenous globular structures for GSE5 and GSE10. The different acid solutions did not influence the TBS to enamel, and the µTBS to dentin was stable over time when dentin was etched with GSE5 and GSE10.

Abstract The aim of this study was to evaluate the thickness of resin cements in the root thirds when using conventional fiberglass posts (CP) and relined fiberglass posts (RP) in weakened roots and to evaluate the morphological characteristics of the dentin-resin interface. Forty human maxillary anterior teeth had the crown sectioned below the cemento-enamel junction. The canals were endodontically treated and weakened with diamond burs. Teeth were divided into four groups (n = 10): Group 1 – CP + RelyX ARC; Group 2 – CP + RelyX U200; Group 3 – RP + RelyX ARC; and Group 4 – RP + RelyX U200. Prior to luting, 0.1% Fluorescein and 0.1% Rhodamine B dyes were added to an adhesive and resin cement, respectively. Slices were obtained from the apical, middle, and cervical thirds of the root. Confocal laser scanning microscopy images were recorded in four areas (buccal, lingual, mesial, distal) of each third. In each area, four equidistant measures of the resin cement were made and the mean value was calculated. The interface morphology was observed. The data were submitted to three-way ANOVA and Tukey’s test (α = 0.05). The interaction between fiberglass posts, resin cement, and root thirds was significant (p < 0.0001). The resin cement thicknesses were significantly lower for RP in comparison with CP, except in the apical third. There was no significant difference between the resin cements for RP. There was formation of resin cement tags and adhesive tags along the root for RP. RP favored the formation of thin and uniform resin cement films and resin tags in weakened roots.